Vinyl Ester Resins

VE resins are a combination of both polyester resin and epoxy resins best properties. While they have high mechanical strength values similar to epoxy resins, they are easy to apply similar to unsaturated polyester resins. They are impact and fatigue resistant, have low water absorbtion values, and excellent electrical and thermal properties. Vinyl ester resins are compatible with glassfiber, carbon fiber, and aramid fibers. Vinyl esters are used for chemical resistant tanks, yachts and wind turbine blades productions. 

Döküm Tipi Vinyl ester resins have low polar groups on chemical backbone and are more resistant to hydrolysis compared to polyester resins.
  •  
  • Product Description
  • Technical Data Sheets
  • Safety Data Sheets
  • Chemical Structure
  • Available Modifications
  • Viscosity
  • Thixotropy
  • Monomer Content
  • Acid Value mg KOH/g
  • Gel Time
  • Tensile Strength
  • Elongation at Break, Tensile
  • Flexural Strength
  • HDT [0,45 MPa]
  • Barcol Hardness, 934
  • Volumetric Shrinkage
  • Remarks
  • Highlights
  • Primary Usages
  • Polives 701
  • High chemical resistant performance vinyl ester
  • PDF
  • PDF
  • VE
  • 400-500
  • N/A
  • 41-43
  • max.9
  • 20-25
  • 80
  • 5
  • 160
  • 100
  • 35
  • 7,7
  • OT1 , OT5
  • - Excellent chemical resistance and mechanical properties
    - Lloyd's Register Approved
    - Excellent hydrolytic resistance
    - Food contact approved
  • GRP structures with exceptional chemical and mechanical strength such as speed crafts, yachts, pipes, automotive parts and chemical linings for pools.
  • Polives 702
  • RTM / Infusion type vinyl ester
  • PDF
  • PDF
  • VE
  • 200-250
  • N/A
  • 43-45
  • max.9
  • 28-32
  • 76
  • 5
  • 155
  • 102
  • 36
  • 7,7
  • OT1 , OT5
  • - Excellent chemical resistance and mechanical properties
    - Lloyd's Register Approved
    - Excellent hydrolytic resistance
    - Excellent fiber wet-out
  • Suitable for infusion production method for marine, military and wind turbine structures.
  • Polives 711
  • High chemical resistant high performance vinyl ester
  • PDF
  • PDF
  • VE
  • 300-400
  • N/A
  • 33-37
  • max. 10
  • 20-30
  • 80
  • 6
  • 160
  • 115
  • 35
  • 7,9
  • OT1 , OT5
  • - High HDT
    - Excellent hydrolytic and chemical resistance
    - Excellent fiber wet-out
    - Excellent mechanical properties
  • GRP structures with exceptional chemical and mechanical strength such as speed crafts, yachts, pipes, automotive parts and chemical linings for pools.
  • Polives 711-I
  • RTM / Infusion type high performance vinyl ester
  • PDF
  • PDF
  • VE
  • 180-200
  • N/A
  • 37-40
  • max. 10
  • 28-32
  • 78
  • 5,5
  • 154
  • 116
  • 36
  • 8
  • OT1 , OT5
  • - High HDT
    - Excellent hydrolytic and chemical resistance
    - Low viscosity
    - Excellent mechanical properties
  • Suitable for infusion production method for marine, military and wind turbine structures.
  • Polives 701-TA
  • Hand lay-up/Spray-up thixotropic preaccelerated performance vinyl ester
  • PDF
  • PDF
  • VE
  • 600-800
  • Tiksotropik
  • 41-44
  • max.9
  • 20-30
  • 80
  • 5
  • 160
  • 100
  • 35
  • 7,7
  • OT1 , OT6
  • - Excellent chemical resistance and mechanical properties
    - Excellent hydrolytic resistance
    - No sagging on vertical surfaces
    - Lloyd's Register approved
  • GRP structures with exceptional chemical and mechanical strength such as speed crafts, yachts, pipes, automotive parts and chemical linings for pools.
  • Polives 711-TA
  • Hand lay-up / Spray-up thixotropic preaccelerated high performance vinyl ester
  • PDF
  • PDF
  • VE
  • 600-800
  • Tiksotropik
  • 38-41
  • max.9
  • 20-30
  • 80
  • 6
  • 160
  • 115
  • 35
  • 7,9
  • OT1 , OT6
  • - High HDT
    - Excellent hydrolytic and chemical resistance
    - Excellent mechanical properties
    - No sagging on vertical surfaces
  • GRP structures with exceptional chemical and mechanical strength such as speed crafts, yachts, pipes, automotive parts and chemical linings for pools.
  • Polives 701-ABP
  • Amine accelerated high chemical resistant performance vinyl ester
  • PDF
  • PDF
  • VE
  • 400-500
  • N/A
  • 38-41
  • max.9
  • 10-15
  • 81
  • 5
  • 130
  • 86
  • 38
  • 7,7
  • OT1 , OT21
  • - High adhesion strength
    - High filler acceptance
    - Suitable for anchoring
    - High chemical resistance
    - Fast curing
  • Anchorage and chemical bolting based on vinyl ester resins.
  • Polives 711-ABP
  • Amine accelerated high chemical resistant high performance vinyl ester
  • PDF
  • PDF
  • VE
  • 300-400
  • N/A
  • 34-39
  • max.9
  • 10-12
  • 80
  • 6
  • 150
  • 107
  • 38
  • 7,9
  • OT1 , OT21
  • - High adhesion strength
    - High filler acceptance
    - Suitable for anchoring
    - High chemical resistance
    - Fast curing
  • Anchorage and chemical bolting based on vinyl ester resins.
  • Polives 710
  • RTM / Infusion type flame retardant vinyl ester
  • PDF
  • PDF
  • VE
  • 400-500
  • N/A
  • 34-38
  • max. 10
  • 20-30
  • 75
  • 3
  • 165
  • 110
  • 35
  • 7,7
  • OT1 , OT5
  • - Increased flame retardancy with antimony
    - High hydrolytic and chemical resistance
    - Excellent fiber wet-out
  • Chemical resistant, flame retardant applications such as boiler units, engine insulation, pipelines and chemical storage tanks and yachts.
  • Polives 721
  • High chemical resistant novolac vinyl ester
  • PDF
  • PDF
  • VE
  • 300-400
  • N/A
  • 36-40
  • max. 15
  • 20-25
  • 82
  • 4
  • 155
  • 140
  • 45
  • 8
  • OT1 , OT5
  • - Excellent chemical resistance and mechanical strength
    - Very high HDT
    - Excellent solvent resistance
  • GRP linings with high chemical resistance, cooling towers and chimneys.

Modification Description

  • FR   Filled flame retardant
  • D*   Filled (*with filler content)
  • T Thixotropic (no sagging)
  • A Cobalt preaccelerated
  • ABP Amine preaccelerated
  • UV UV Curing
  • L   UV light stabilized
  •   I Lower viscosity
  •   V Higher viscosity
  •   LSE   LSE (low styrene emission)
  •   H* Gel time customized (at room temperature) * minutes
  • H40 Optimized for summer season. Gel time (at room temperature) 40 minutes.
  • H20 Optimized for winter season. Gel time (at room temperature) 20 minutes.
  •   COLOR   White or custom color options

Gelcoat Customizations
Polijel gelcoat table descriptions and modifications.

  • Spray Application (airless preferred)
  • Brush or Roller Application
  • Color Option: White colored
  • Color Option: Light colored (pastel)
  • Color Option: PRO colored

Production Quantity Depending on Process (parts/year)
Regardless of product dimension and complexity..

İlk sen haberdar ol!
Poliya’nın güncel haberlerinden ve yeni ürünlerinden haberdar olmak ister misiniz?
İzin ver Daha Sonra
x

Haberlerden Geri Kalmayın

En son haberlerimizden ve ürünlerimizden ilk haberdar olmak için lüten aşağıdaki alanları doldurunuz..