Low Styrene Emission / LSE

Styrene evaporation in hand lay-up and spray-up production may cause VOC emission problems in the work environment. The low styrene content and low styrene emission resins in this product group offer a safer working environment for workers by lowering the amount of styrene evaporation. 

Döküm Tipi LSE type resins suppress the styrene evaporation and provide for a safer environment.
  • Chemical Resistance Guide
  • Refer to our Chemical Resistance Guide for more information about use of resins in different chemical environments.
SONRAKİ ÖNCEKİ
  •  
  • Product Description
  • Technical Data Sheets
  • Safety Data Sheets
  • Chemical Structure
  • Available Modifications
  • Viscosity
  • Gel Time
  • Tensile Strength
  • Elongation at Break,Tensile
  • Volumetric Shrinkage
  • Barcol Hardness, 934
  • Tmax
  • Thixotropy
  • Remarks
  • Highlights
  • Primary Usages
  • Polipol 3401-TA-LSE-H40
  • Hand lay-up / Spray-up thixotropic preaccelerated LSE polyester
  • PDF
  • PDF
  • Ortho
  • 500-600
  • 38-42
  • 71
  • 2,6
  • 7,4
  • 40
  • 140
  • Tiksotropik
  • OT1 , OT4
  • - Low styrene emission
    - No sagging on vertical surfaces.
    - Quick and easy fiber wet-out
    - Lloyd's Register approved
  • Bumpers, fenders, cabinets, pool filters, industrial GRP parts such as vehicle parts.
  • Polipol 3401-TALSE- H20-White
  • Hand lay-up / Spray-up thixotropic preaccelerated LSE white polyester
  • PDF
  • PDF
  • Ortho
  • 800-900
  • 19-21
  • 71
  • 2,6
  • 7,4
  • 40
  • 140
  • Tiksotropik
  • OT1 , OT4
  • - White colored
    - Low styrene emission
    - No sagging on vertical surfaces
    - Quick and easy fiber wet-out
    - Lloyd's Register approved
  • Bumpers, fenders, cabinets, pool filters, industrial GRP parts such as vehicle parts.
  • Polipol 339-TA-LSE-H40
  • Hand lay-up / Spray-up medium reactivity thixotropic preaccelerated LSE polyester
  • PDF
  • PDF
  • Ortho
  • 600-800
  • 38-42
  • 68
  • 2,2
  • 8,2
  • 48
  • 180
  • Tiksotropik
  • OT1 , OT4
  • - Summer version
    - Excellent fiber wet-out
    - Low styrene emission
    - No sagging on vertical surfaces
    - Good mechanical properties
    - Optimum HDT
  • AC units and system components, applications which require mechanical strength such as GRP parts for marine and automotive industry.
  • Polipol 339-TA-LSE-H20
  • Hand lay-up / Spray-up thixotropic preaccelerated LSE polyester
  • PDF
  • PDF
  • Ortho
  • 600-800
  • 19-21
  • 68
  • 2,2
  • 8,2
  • 48
  • 180
  • Tiksotropik
  • OT1 , OT4
  • - Excellent fiber wet-out
    - Good mechanical properties
    - Optimum HDT
    - Low styrene emission
    - No sagging on vertical surfaces
  • AC units and system components, applications which require mechanical strength such as GRP parts for marine and automotive industry.
  • Polipol 351-TALSE- H40
  • Hand lay-up / Spray-up medium/high reactivity thixotropic preaccelerated LSE polyester
  • PDF
  • PDF
  • Ortho
  • 600-800
  • 38-42
  • 65
  • 2
  • 8,95
  • 46
  • 190
  • Tiksotropik
  • OT1 , OT4
  • - High HDT and mechanical values
    - Fast demolding
    - Low styrene emission
    - No sagging on vertical surfaces
  • Industrial GRP parts which require thermal resistance.
  • Polipol 351-TA-LSE-H20
  • Hand lay-up / Spray-up high reactivity thixotropic preaccelerated LSE polyester
  • PDF
  • PDF
  • Ortho
  • 600-800
  • 19-21
  • 65
  • 2
  • 8,95
  • 46
  • 190
  • Tiksotropik
  • OT1 , OT4
  • - High HDT and mechanical values
    -Fast demolding time
    - Low styrene emission
    - No sagging on vertical surfaces
  • GRP parts which require heat resistance.
  • Polipol 3471-TA-LSE
  • Hand lay-up / Spray-up thixotropic preaccelerated LSE polyester
  • PDF
  • PDF
  • Ortho
  • 600-800
  • 18-22
  • 72
  • 2,4
  • 8,2
  • 50
  • 195
  • Tiksotropik
  • OT1 , OT4
  • - Minimal shape deformation
    - Excellent HDT
    - Fast demolding time
    - Low styrene emission
  • GRP parts which require high temperature resistance such as automobile and enginee hood, body and roofs.
  • Polipol 3872-TA-LSE-H40
  • Hand lay-up / Spray-up thixotropic preaccelerated LSE polyester
  • PDF
  • PDF
  • Ortho
  • 600-800
  • 35-40
  • 75
  • 4,2
  • 8,7
  • 42
  • 190
  • Tiksotropik
  • OT1 , OT4
  • - Very good fiber wet-out
    - Chemical resistance against many chemicals. (ref CRG)
    - Excellent mechanical values
    - Lloyd's Register approved
  • GRP parts which require flexibility and mechanical strength, linings that require resistance to weak alkaline and acidic environments.
  • Polipol 344-TA-LSE
  • Hand lay-up / Spray-up medium/high reactivity thixotropic preaccelerated LSE polyester
  • PDF
  • PDF
  • THPA
  • 600-800
  • 12-20
  • 70
  • 2,3
  • 8,2
  • 43
  • 190
  • Tiksotropik
  • OT1 , OT4
  • - MAN Nuremberg Lab 3F approved
    - Excellent HDT and mechanical properties
    - DIN 16946/2: Type 1140
  • GRP parts which require thermal resistance such as vehicle and machinery hoods and engine components.
  • Polipol 3469-TA-LSE
  • Hand lay-up / Spray-up medium/high reactivity thixotropic preaccelerated LSE polyester
  • PDF
  • PDF
  • DCPD
  • 600-700
  • 27-29
  • 70
  • 2,46
  • 6
  • 44
  • 150
  • Tiksotropik
  • OT1 , OT4
  • - Special DCPD structure
    - High quality surface
    - Excellent fiber wet-out
    - Low styrene emission
    - Low volumetric shrinkage
  • Components that require high surface quality especially for commercial vehicles and truck GRP part productions.

Packing Types

You can choose any package type suitable for your production system or you can get further information from our sales department regarding container options.

Contact Sales

  • 5 Kg
    Mini Bucket

Modification Description

  • FR   Filled flame retardant
  • D*   Filled (*with filler content)
  • T Thixotropic (no sagging)
  • A Cobalt preaccelerated
  • ABP Amine preaccelerated
  • UV UV Curing
  • L   UV light stabilized
  •   I Lower viscosity
  •   V Higher viscosity
  •   LSE   LSE (low styrene emission)
  •   H* Gel time customized (at room temperature) * minutes
  • H40 Optimized for summer season. Gel time (at room temperature) 40 minutes.
  • H20 Optimized for winter season. Gel time (at room temperature) 20 minutes.
  •   COLOR   White or custom color options

Gelcoat Customizations
Polijel gelcoat table descriptions and modifications.

  • Spray Application (airless preferred)
  • Brush or Roller Application
  • Color Option: White colored
  • Color Option: Light colored (pastel)
  • Color Option: PRO colored

Production Quantity Depending on Process (parts/year)
Regardless of product dimension and complexity..

İlk sen haberdar ol!
Poliya’nın güncel haberlerinden ve yeni ürünlerinden haberdar olmak ister misiniz?
İzin ver Daha Sonra
x

Haberlerden Geri Kalmayın

En son haberlerimizden ve ürünlerimizden ilk haberdar olmak için lüten aşağıdaki alanları doldurunuz..