ZERO RTM System
Polipol 3387-ZERO is a zero shrink resin which is specially designed for RTM productions. It provides exceptional dimensional stability and excellent surface quality. When Polipol 3387- ZERO is used as RTM resin in molds produced with Polipol 321- ZERO tooling resin, it is possible to obtain a high degree of dimensional conformity to model and design.
ZERO RTM System Components
① ZERO Tooling Resin (for mold making)
② Gelcoat – Polijel 210, 212, 213 or 215 (depends on performance needed)
③ RTM Resin – Polipol 3387-ZERO
ZERO Tooling System Components
① Tooling Gelcoat – Polijel P-272 or P-220 (depends on performance needed)
② Barrier Coat – Polijel BC-782
③ Skin Coat – Polives 701-TA
④ Tooling Resin – Polipol 321-ZERO
It is possible to produce flat, corrugated, transparent or colored sheets at a high processing speed with continuous laminating.
Chemical Resistance Guide
Refer to our Chemical Resistance Guide for more information about use of resins in different chemical environments.
ZERO RTM System
Polipol 3387-ZERO is a zero shrink resin which is specially designed for RTM productions. It provides exceptional dimensional stability and excellent surface quality. When Polipol 3387- ZERO is used as RTM resin in molds produced with Polipol 321- ZERO tooling resin, it is possible to obtain a high degree of dimensional conformity to model and design.
ZERO RTM System Components
① ZERO Tooling Resin (for mold making)
② Gelcoat – Polijel 210, 212, 213 or 215 (depends on performance needed)
③ RTM Resin – Polipol 3387-ZERO
ZERO Tooling System Components
① Tooling Gelcoat – Polijel P-272 or P-220 (depends on performance needed)
② Barrier Coat – Polijel BC-782
③ Skin Coat – Polives 701-TA
④ Tooling Resin – Polipol 321-ZERO
| Test | Method | Polipol 3387 ZERO | Lamination of 4 layers of Chopped Strand Mat 450gr/m2 |
||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Flexural Strength (MPa) | ISO 0178 | 120 | 270 | ||||||||||
| Modulus of Elasticity, Flexural (MPa) | ISO 0178 | 3700 | 8300 | ||||||||||
| Elongation at Break, Flexural (%) | ISO 0178 | 3.5 | 5.8 | ||||||||||
| Tensile Strength (MPa) | ISO 0527 | 62 | 140 | ||||||||||
| Modulus of Elasticity, Tensile (MPa) | ISO 0527 | 2950 | 6800 | ||||||||||
| Elongation at Break, Tensile (%) | ISO 0527 | 2.4 | 3.8 | ||||||||||
| Izod Impact Strenght (kj/m2) | ISO 0180 | 8 | 13 | ||||||||||
| HDT [0,45 MPa] (°C) | ISO 0075-B | 115 | - | ||||||||||
| Glass Transition Temperature (°C) | ASTM-E 1640-04 | 127 | - | ||||||||||
| Water Absorption (%) | ISO 0062 | 0.17 | - | ||||||||||
| Barcol Hardness, 934 (Barkol) | ASTM-D 2583 | 44 | - | ||||||||||
| Lineer Shrink (%) | ASTM-C 356 | 0.05 | - | ||||||||||
Previous
Next
Packing Types
You can choose any package type suitable for your production system or you can get further information from our sales department regarding container options.
Modification Description
- FR Filled flame retardant
- D* Filled (*with filler content)
- T
Thixotropic (no sagging)
- A
Cobalt preaccelerated - ABP Amine preaccelerated
- UV UV Curing
- L UV light stabilized
- I
Lower viscosity - V Higher viscosity
- LSE LSE (low styrene emission)
- H*
Gel time customized (at room
temperature) * minutes 
H40 Optimized for summer season.
Gel
time (at room temperature) 40 minutes.
H20 Optimized for winter season.
Gel
time (at room temperature) 20 minutes.- COLOR White or custom color options
Gelcoat Customizations
Polijel gelcoat table descriptions and modifications.
Spray
Application (airless preferred)
Brush or Roller
Application
Color Option:
White colored
Color
Option: Light colored (pastel)
Color Option:
PRO
colored
Production Quantity Depending on Process (parts/year)
Regardless of product dimension and complexity..