The low styrene content and styrene free resin group contains resins that can be used in various applications from continuous lamination to hand lay-up applications, and from model production to paste production. It helps to reduce styrene emissions with the use of appropriate monomers instead of styrene monomer in vinylester, DCPD, isophthalic, amine accelerated resin chemistries. Styrene free resin systems provides elimination of production disadvantages caused by styrene monomer with resins that do not contain styrene.
Styrene free resin systems provides elimination of production disadvantages caused by styrene monomer.
Styrene Free and Low Styrene Resin Systems
The low styrene content and styrene free resin group contains resins that can be used in various applications from continuous lamination to hand lay-up applications, and from model production to paste production. It helps to reduce styrene emissions with the use of appropriate monomers instead of styrene monomer in vinylester, DCPD, isophthalic, amine accelerated resin chemistries. Styrene free resin systems provides elimination of production disadvantages caused by styrene monomer with resins that do not contain styrene.
Buildings and Construction
Mold and Pattern
Plant Enclosures
Chemical Bolting and Anchoring Systems
Pipe Rehabilitation
- Product Description
- Chemical Structure
- Available Modifications
- Viscosity
- Thixotropy
-
Monomer Content
-
Gel Time
-
Tmax
-
Tensile Strength
-
Elongation at Break, Tensile
-
Flexural Strength
-
HDT [0,45 MPa]
-
Barcol Hardness, 934
-
Volumetric Shrink
- Remarks
- Highlights
- Primary Usages
-
Polipol 760-V
New - Low styrene content polyester
- DCPD
- 400-500
- N/A
- 25-30
- 19-21
- 155
- 60
- 2,5
- 127
- 74
- 42
- 6,5
-
OT1 , OT2 - - Low
viscosity
- Excellent fiber wetting
- Low shrinkage
- High filler capacity
- Components that require high surface quality especially for commercial vehicles and truck GRP part productions
-
Polipol 760-TA
New - Hand lay-up / Spray-up thixotropic preaccelerated polyester
- DCPD
- 600-700
- Thixotropic
- 36-42
- 20-30
- 140
- 56
- 2,7
- 122
- 80
- 43
- 7,4
-
OT1 , OT4 - - Low
volumetric shrink
- Excellent fiber wet-out
- Thixotropic, no sagging on vertical surfaces
- High-quality composite surface
- Components that require high surface quality especially for commercial vehicles and truck GRP part productions.
-
Polipol 602
New - Styrene free polyester
- ISO
- 600-800
- N/A
- 36-39
- 16-18
- 180
- 69
- 2,7
- 126
- 104
- 44
- 8,0
-
OT1 , OT2 - - Very
good mechanical values
- Excellent fiber wetting
- High HDT value
- Chemical resistance
- Styrene free
- Productions that require no styrene smell.
-
Polipol 602-ABP
New - Amine accelerated rapid curing styrene-free marble adhesive polyester
- ISO
- 500-700
- N/A
- 36-39
- 8-9
- 175
- 73
- 2,5
- 140
- 92
- 46
- -
-
OT1 , OT19 - -
Styrene free
- High reactivity
- Fast curing
- High filler acceptance
- Styrene-free polyester repair putty, anchorage or chemical bolting, and marble adhesive.
-
Polipol 3515
- Polystyrene foam coating polyester
- Ortho
- 1000-1500
- N/A
- 35-39
- 10-17
- 190
- 50
- 5,5
- 120
- 65
- -
- 7,5
-
OT1 , - -
Styrene free
- Does not melt polystyrene foam
- Composite shell for polystyrene mold patterns.
-
Polipol 3890-T
New - Pipe rehabilitation type styrene free thixotropic isopthalic resin
- ISO
- 1700-2000
- Thixotropic
- 39-43
- 20-25
- 170
- 67
- 3
- 125
- 100
- 43
- 8,1
-
OT1 , - -
Styrene free
- Suitable for steam curing
- Rehabilitation of old pipes with CIPP method.
-
Polives 708-ABP
New - Amine accelerated styrene free vinyl ester
- VE
- 1000-1400
- N/A
- 34-39
- 10-12
- 130
- N/A
- N/A
- N/A
- N/A
- N/A
- N/A
-
OT1 , OT2 - -
Styrene free odorless formula
- Improved shelf life
- High chemical resistance and mechanical strength
- Excellent adhesion
- Strene-free VE for repairing putty, chemical bolting, and marble adhesive.
-
Polipol 2215
New - Continous lamination type high performance low styrene content gelcoat
- ISO
- 500-600
- N/A
- -
- 20-25
- -
- -
- -
- -
- -
- -
- -
-
OT1 , OT2 - -
Durable and flexible gel-coat
- Very good atmospheric weathering resistance.
- Very flexible gel-coat for flexible flat panels
- Composite panel productions with continous lamination.
Packing Types
You can choose any package type suitable for your production system or you can get further information from our sales department regarding container options.
Modification Description
- FR Filled flame retardant
- D* Filled (*with filler content)
- T Thixotropic (no sagging)
- A Cobalt preaccelerated
- ABP Amine preaccelerated
- UV UV Curing
- L UV light stabilized
- I Lower viscosity
- V Higher viscosity
- LSE LSE (low styrene emission)
- H* Gel time customized (at room temperature) * minutes
- H40 Optimized for summer season. Gel time (at room temperature) 40 minutes.
- H20 Optimized for winter season. Gel time (at room temperature) 20 minutes.
- COLOR White or custom color options
Gelcoat Customizations
Polijel gelcoat table descriptions and modifications.
- Spray Application (airless preferred)
- Brush or Roller Application
- Color Option: White colored
- Color Option: Light colored (pastel)
- Color Option: PRO colored